Compression breaking load: 972 Kg/cm2
Compression breaking load after freezing test: 867 Kg/cm2
Bending Strength: 196 Kg/cm2
Volumetric Weight: 2515 Kg/m3
Water absorption at N.P. conditions: 2,34 %
Apparent porosity: 5,9 %
Thermal linear expansion coefficient: 5,3×10-6 per ̊C
Abrasion Test: 4 mm
Impact Test: minimum fall height: 40 cm
“Pulido
Ablandado
Envejecido
Lijado
Martillado”
Cortado à medida
Ladrilhos
Chapas
Blocos
Compression breaking load: 972 Kg/cm2
Compression breaking load after freezing test: 867 Kg/cm2
Bending Strength: 196 Kg/cm2
Volumetric Weight: 2515 Kg/m3
Water absorption at N.P. conditions: 2,34 %
Apparent porosity: 5,9 %
Thermal linear expansion coefficient: 5,3×10-6 per ̊C
Abrasion Test: 4 mm
Impact Test: minimum fall height: 40 cm
Polido
Amaciado
Envelhecido
Areado
Bujardado
Coupé à la taille
Carrelage
Dalles
Blocs
Charge de rupture par compression: 972 Kg / cm2
Charge de rupture par compression après test de gel: 867 Kg / cm2
Résistance à la flexion: 196 Kg / cm2
Poids volumétrique: 2515 Kg / m3
Absorption d’eau à N.P. conditions: 2,34%
Porosité apparente: 5,9%
Coefficient de dilatation linéaire thermique: 5,3×10-6 par ̊C
Test d’abrasion: 4 mm
Test d’impact: hauteur de chute minimale: 40 cm
Brillant
Adouci
Vieilli
Poncé
Martelé
Cut to size
Tiles
Slabs
Blocks
Compression breaking load: 972 Kg/cm2
Compression breaking load after freezing test: 867 Kg/cm2
Bending Strength: 196 Kg/cm2
Volumetric Weight: 2515 Kg/m3
Water absorption at N.P. conditions: 2,34 %
Apparent porosity: 5,9 %
Thermal linear expansion coefficient: 5,3×10-6 per ̊C
Abrasion Test: 4 mm
Impact Test: minimum fall height: 40 cm
Polished
Softened
Aged
Sanded
Hammered